Advertorial - 3D-printed helicopter blade mold
Photo Credit: Thermwood Corp

Advertorial - 3D-printed helicopter blade mold

Advertorial - Additive Manufacturing Target Guide 2019

Joint venture between Thermwood and Bell creates large, 3D-printed autoclavable tools.

Subscribe
February 28, 2019

Expensive, long-lead time tooling can limit aerospace development. To help solve this challenge, Bell engineers reached out to Thermwood, developer of large-scale additive manufacturing (LSAM) technology.

The Thermwood team offered Bell Flight the capabilities of 60mm melt core technology for manufacturing large-bond tooling.

Bell responded by providing Thermwood a model of a closed-cavity blade mold measuring 240" x 14" x 17".

Basic tooling requirements were:

  • Must be printed in one continuous run for vacuum integrity
  • Surface finish must be 32rms or better
  • Tooling must withstand 90psi at 360°F
  • Tight tolerances, features to ensure proper mating of the two blade-mold halves

The process

Upon receiving the model and requirements, the Thermwood team began to print the tool in one continuous run using Techmer PM’s 25% carbon fiber-reinforced PESU (polyethersulfone), a material formulated for LSAM printing.

One tool-half was printed in 3 hours, 8 minutes, weighing 542 lb using the 60mm melt core installed on Thermwood’s LSAM system at its Southern Indiana Development/Demonstration Lab.

Continuous-cooling print process

With Thermwood’s room-temperature, continuous-cooling print process, the cycle time for each layer is determined solely by how long it takes a printed polymer to cool enough so it’s ready to accept the next layer.

Printing at the proper temperature achieves a fused, void-free printed structure that will maintain vacuum in an autoclave without a coating. The print head output determines how much material can be printed while the layer cools. Bigger print heads make larger parts, not necessarily faster print times.

3D-printed wave structures support a closed-cavity blade mold without touching cavity’s back.
Photo Credit: Thermwood Corp

The 60mm melt core has a maximum output of 480 lb/hr to 570 lb/hr, depending on the polymer. It can print more than 100ft of typical 0.830" x 0.200" print bead per minute. This high print rate, even with high-temperature material, allows orienting the print bead along the tool’s length where thermal expansion is lower, minimizing tool expansion and contraction with temperature changes.

Internal support structure

The tool’s internal printed structure supports the mold without touching the back of the mold cavity, allowing air to flow freely under the entire formed part in the autoclave, for easier, more consistent part-curing. Incorporating complex internal structures is possible with Thermwood’s LSAM Print 3D slicing software.

Multiple processes

The LSAM can print, trim, and drill to specifications. The team machined the printed, lower blade mold-half using the LSAM’s subtractive ability in 40 hours.

The Thermwood team will print the second half of the blade mold so Bell engineers can cure a full, molded blade within the complete additively-manufactured bond tool.

Blade mold being printed in Thermwood’s LSAM.

“This raises additive manufacturing to a new level, opening opportunities only dreamed of a few years ago,” says Ken Susnjara – Thermwood’s founder, chairman, and CEO.

LSAM advances – vertical layer printing, changeable melt cores, polymers tailored for LSAM processing – are opening new possibilities for additive production of larger, more complex components.

Bell Flight
https://www.bellflight.com

Techmer PM
https://www.techmerpm.com

Thermwood Corp
http://www.thermwood.com